hydrogen embrittlement

hydrogen embrittlement什么意思,hydrogen embrittlement翻译

基本解释

un.: 氢脆
网络: 氢脆性；氢脆化；氢脆变

英汉解释

• 氢脆

例句

• Acoustic-emission techniques have been used to determine the rate of cracking of highstrength steel due to hydrogen embrittlement.

  声发射技术已被用来确定高强钢因氢脆而开裂的速率。

• Hydrogen embrittlement is an outstanding problem when high strength aluminium alloys are applied in the corrosive environment.

  氢脆是高强度铝合金在腐蚀环境中应用遇到的突出问题。

• Rework that requires low-hydrogen embrittlement (LHE) cadmium stylus plating should be performed when the component is not loaded.

  翻修要求的低氢脆（LHE）镀镉应当在部件不在翼的状态下进行。

• Results show that the alloy in aging state, especially in deformation-aging state, is apparently susceptible to hydrogen embrittlement.

  结果表明，时效状态、特别是形变时效状态合金具有明显的氢脆敏感性。

• This failure, which may occur in a short period of time and often is evidenced by cracks in the steel, is called hydrogen embrittlement.

  这种损坏可能在短时间内产生，常表现为在钢上发生肉眼可见的裂纹，称为氢蚀致脆，简称氢脆。

• Figure 17 is a scanning electron microscope view of a typical hydrogen embrittlement crack where separation occurs along grain boundaries.

  图17示意了用电子显微镜扫描出的沿晶粒边界产生的氢脆裂纹。

• The results of the experiment show that it is effective to prevent hydrogen embrittlement failure by hardening and tempering treatment.

  实验结果表明：进行调质预处理是防止氢脆失效较为有效的方法。

• The reason for hydrogen embrittlement fracture is incomplete removal of hydrogen after acid-washing or electroplating.

  是在酸洗电镀后除氢不及时或不彻底导致氢脆断裂。

• Hydrogen embrittlement is not a major influence on fatigue life.

  此外实验证明氢脆并不是影响电刷镀试件疲劳寿命的主要原因。

• Hydrogen embrittlement can become important in martensitic steels.

  马氏体钢容易出现氢脆现象。